| POM 900P 美國杜邦公司 物性數(shù)據(jù) |
| 規(guī)格級別： | 注塑級 | 外觀顏色： | --- |
| 用途概述： | 較多模穴與較不易填充的薄肉成型品。 | ||
| 備注說明： | 加工特性：高流動性低黏度表面經(jīng)潤滑樹脂，DELRIN 900P有優(yōu)異的成型特性。產品：與DELRIN 500相近，但稍微低的拉伸延伸率和沖擊強度。 | ||
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 物理性能 | 比重 | --- | ASTM D-792 | 1.42 | --- |
| 吸水量 | 24小時浸漬 | ASTM D-570 | 0.25 | % | |
| 吸水量 | 50%相對濕度 | ASTM D-570 | 0.22 | % | |
| 吸水量 | 浸漬平衡點 | ASTM D-570 | 0.90 | % | |
| 模收縮 | --- | --- | 2.2-2.4 | % | |
| 機械性能 | 洛氏硬度M | --- | ASTM D-785 | 94 | --- |
| 洛氏硬度R | --- | ASTM D-785 | 120 | --- | |
| 拉伸強度 | -55℃ | ASTM D-638 | 101 | MPa | |
| 拉伸強度 | 23℃ | ASTM D-638 | 69 | MPa | |
| 拉伸強度 | 70℃ | ASTM D-638 | 48 | MPa | |
| 拉伸強度 | 100℃ | ASTM D-638 | 36 | MPa | |
| 拉伸強度 | 122℃ | ASTM D-638 | 26 | MPa | |
| 破裂點拉伸變形量 | -55℃ | ASTM D-638 | 10 | % | |
| 破裂點拉伸變形量 | 23℃ | ASTM D-638 | 25 | % | |
| 破裂點拉伸變形量 | 70℃ | ASTM D-638 | 180 | % | |
| 破裂點拉伸變形量 | 100℃ | ASTM D-638 | >260 | % | |
| 破裂點拉伸變形量 | 122℃ | ASTM D-638 | >260 | % | |
| 彈性系數(shù) | 23℃ | ASTM D-638 | 3640 | MPa | |
| 撓曲系數(shù) | -55℃ | ASTM D-790 | 4730 | MPa | |
| 撓曲系數(shù) | 23℃ | ASTM D-790 | 3220 | MPa | |
| 撓曲系數(shù) | 70℃ | ASTM D-790 | 1720 | MPa | |
| 撓曲系數(shù) | 100℃ | ASTM D-790 | 1030 | MPa | |
| 撓曲系數(shù) | 122℃ | ASTM D-790 | 755 | MPa | |
| 撓曲變形強度 | 23℃ | ASTM D-790 | 97 | MPa | |
| 壓縮應力 | 23℃,1%變形 | ASTM D-695 | 35 | MPa | |
| 壓縮應力 | 23℃,10%變形 | ASTM D-695 | 121 | MPa | |
| 抗剪強度 | 23℃ | ASTM D-732 | 66 | MPa | |
| 撓曲疲勞忍耐限度 | 50%RH,23℃,106周期 | ASTM D-671 | 32 | MPa | |
| 負載變形量 | 140kg/cm2,50℃ | ASTM D-621 | 0.5 | % | |
| 抗拉伸沖擊強度 | 長試片23℃ | ASTM D-1822 | 250 | kj/m2 | |
| IZOD沖擊強度 | 無缺口23℃ | ASTM D-256 | 1620 | j/m | |
| IZOD沖擊強度 | 缺口-40℃ | ASTM D-256 | 55 | j/m | |
| IZOD沖擊強度 | 23℃ | ASTM D-256 | 71 | j/m | |
| 電氣性能 | 抗電弧 | 3.1mm | ASTM D-495 | 220 | sec |
| 介電強度 | 瞬間Short time(2.3mm) | ASTM D-149 | 19.7 | kv/mm | |
| 容積電阻率 | 23℃,0.2%含水量 | ASTM D-257 | 1×1015 | Ω.cm | |
| 介電常數(shù) | 50%RH,23℃,102～106Hz | ASTM D-150 | 3.7 | Ω.cm | |
| 介電因數(shù) | 50%RH,23℃,106Hz | ASTM D-150 | 0.005 | --- | |
| 熱 性 能 | 線性熱膨脹系數(shù) | 60～104℃ | ASTM D-696 | 13.7 | 10-5m/m℃ |
| 線性熱膨脹系數(shù) | 104～160℃ | ASTM D-696 | 14.9 | 10-5m/m℃ | |
| 自燃性 | --- | UL 94 | HB | --- | |
| 熱畸變溫度 | 1.8MPa | ASTM D-648 | 136 | ℃ | |
| 熱畸變溫度 | 0.5MPa | ASTM D-648 | 172 | ℃ | |
| 熔點 | ℃ | ASTM D-2133 | 175 | --- | |
| 熱傳導系數(shù) | --- | --- | 0.37 | W/mk | |
| 線性熱膨脹系數(shù) | -40～29℃ | ASTM D-696 | 10.4 | 10-5m/m℃ | |
| 線性熱膨脹系數(shù) | 29～60℃ | ASTM D-696 | 12.2 | 10-5m/m℃ | |