杜邦PA6 ZYTEL 73G45L 產品特性：含45%玻纖增強，自潤滑，高光澤，良好的剛性，良好的強度，良好的表面光潔度，用于家電部件，體育用品，高光閃點等應用
我公司提供的產品均為正牌塑膠原料，品質保證，貨源穩(wěn)定，送貨上門，可免費提供官方物性表、UL黃卡，并隨貨提供RoHS報告、SGS報告等，索取權威資料請致電13268582149
PA6 73G45L 物性表：
| Physical |
Dry |
Conditioned |
Unit |
Test Method |
| Density |
1.51 |
-- |
g/cm³ |
ISO 1183 |
| Molding Shrinkage - Flow |
|
|
|
Internal Method |
| 1.60 mm |
0.10 |
-- |
% |
|
| 3.20 mm |
0.20 |
-- |
% |
|
| Molding Shrinkage - Across Flow |
|
|
|
Internal Method |
| 1.60 mm |
1.0 |
-- |
% |
|
| 3.20 mm |
0.90 |
-- |
% |
|
| Molding Shrinkage |
|
|
|
ISO 294-4 |
| Across Flow: 2.00 mm |
0.90 |
-- |
% |
|
| Flow: 2.00 mm |
0.15 |
-- |
% |
|
| Water Absorption (Saturation, 23°C) |
4.9 |
-- |
% |
ISO 62 |
| Water Absorption (Equilibrium, 23°C, 50% RH) |
1.5 |
-- |
% |
ISO 62 |
| Mechanical |
Dry |
Conditioned |
Unit |
Test Method |
| Tensile Modulus (23°C) |
14500 |
9700 |
MPa |
ISO 527-2 |
| Tensile Strength (23°C) |
214 |
145 |
MPa |
ASTM D638 |
| Tensile Stress (Break, 23°C) |
230 |
160 |
MPa |
ISO 527-2 |
| Tensile Elongation (Break, 23°C) |
3.0 |
5.0 |
% |
ASTM D638 |
| Tensile Strain (Break, 23°C) |
3.0 |
5.0 |
% |
ISO 527-2 |
| Tensile Creep Modulus (1 hr) |
-- |
9400 |
MPa |
ISO 899-1 |
| Tensile Creep Modulus (1000 hr) |
-- |
7300 |
MPa |
ISO 899-1 |
| Flexural Modulus (23°C) |
12100 |
7000 |
MPa |
ASTM D790 |
| Flexural Modulus (23°C) |
13000 |
-- |
MPa |
ISO 178 |
| Impact |
Dry |
Conditioned |
Unit |
Test Method |
| Charpy Notched Impact Strength |
|
|
|
ISO 179/1eA |
| -30°C |
19 |
23 |
kJ/m² |
|
| 23°C |
20 |
25 |
kJ/m² |
|
| Charpy Unnotched Impact Strength |
|
|
|
ISO 179/1eU |
| -30°C |
120 |
100 |
kJ/m² |
|
| 23°C |
120 |
110 |
kJ/m² |
|
| Notched Izod Impact (23°C) |
190 |
240 |
J/m |
ASTM D256 |
| Notched Izod Impact Strength |
|
|
|
ISO 180/1A |
| -30°C |
15 |
-- |
kJ/m² |
|
| 23°C |
18 |
24 |
kJ/m² |
|
| Unnotched Izod Impact (23°C) |
1500 |
1500 |
J/m |
ASTM D4812 |
| Thermal |
Dry |
Conditioned |
Unit |
Test Method |
| Deflection Temperature Under Load (0.45 MPa, Unannealed) |
221 |
-- |
°C |
ASTM D648 |
| Heat Deflection Temperature (0.45 MPa, Unannealed) |
221 |
-- |
°C |
ISO 75-2/B |
| Deflection Temperature Under Load (1.8 MPa, Unannealed) |
213 |
-- |
°C |
ASTM D648 |
| Heat Deflection Temperature (1.8 MPa, Unannealed) |
213 |
-- |
°C |
ISO 75-2/A |
| Melting Temperature 2 |
221 |
-- |
°C |
ISO 11357-3 |
| CLTE - Flow (23 to 55°C) |
0.000016 |
-- |
cm/cm/°C |
ASTM E831 |
| CLTE - Flow (23 to 55°C) |
0.000016 |
-- |
cm/cm/°C |
ISO 11359-2 |
| CLTE - Transverse (23 to 55°C) |
0.00010 |
-- |
cm/cm/°C |
ASTM E831 |
| CLTE - Transverse (23 to 55°C) |
0.00010 |
-- |
cm/cm/°C |
ISO 11359-2 |
| Flammability |
Dry |
Conditioned |
Unit |
Test Method |
| Flame Rating - UL (1.50 mm) |
HB |
-- |
|
UL 94 |