| 項 目 Property |
單 位 Unit |
試驗方法 Test Method |
試驗條件 Test Condition |
K7025 | |
| 熔融指數(shù) Melt Flow Index |
g/10 min | ASTM D-1238 |
230℃×2.16Kg | 25.0 | |
|
降伏點(diǎn)抗張強(qiáng)度 |
kg/cm2 | ASTM D-638 |
23℃ | 270 | |
| 斷裂點(diǎn)延伸率 Tensile Elongation at Break |
% | ASTM D-638 |
23℃ | ＞200 | |
| 彎曲模數(shù) Flexural Modulus |
kg/cm2 | ASTM D-790A |
23℃ | 12500 | |
| 硬度 Hardness |
R-Scale | ASTM D-785 |
23℃ | 95 | |
| Izod衝擊強(qiáng)度 Izod Impact Strength |
kg-cm/cm | ASTM D-256 |
23℃ 1/8'' 厚 |
23℃ | 8.0 |
| - 20℃ | 4.5 | ||||
| 熱變形溫度 Heat Deflection Temperature |
℃ | ASTM D-648 at 4.6kg/cm2 |
Unannealed 1/4'' 厚 |
120 | |
| 收縮率 Molding Shrinkage |
% | FCFC Method |
23℃ | 1.4~1.8 | |
| 比 重 Specific Gravity |
ASTM D-792 |
23℃/23℃ | 0.90 | ||
| FDA Compliance |
21 CFR Pt 177.1520 |
Yes | |||