| Physical | Nominal Value | Unit | Test Method |
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 8.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (80°C, 3.00 mm) | 0.50 to 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
| Tensile Stress (Yield) | 62.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 7.0 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 100 | % | ISO 527-2 |
| Flexural Modulus | 2400 | MPa | ISO 178 |
| Flexural Strength | 93.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
| Charpy Notched Impact Strength 2 | 16 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 124 | °C | ISO 75-2/A |
| CLTE - Flow | 0.000065 | cm/cm/°C | ISO 11359-2 |
| CLTE - Transverse | 0.000066 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Unit | Test Method |
| Flame Rating - UL (2.00 mm) | V-0 | UL 94 | |
| Optical | Nominal Value | Unit | Test Method |
| Transmittance | ASTM D1003 | ||
| 2000 µm | 88.0 | % | |
| 3000 µm | 88.0 | % |